Iron Ore Fines [ Code : VM - 001 ]
Chemical composition : Fe. 63.5% basis. Rejection : Below 626% Fe; Silica : 3.5% max.; Alumina : 3.5% max.; Sulphur : 0.05% max.; Phosphorous : 0.08% max.; Moisture : 8% max.. |
 |
Manganese Ore [ Code : VM - 002 ]
Chemical composition : Di Oxide grade + 74 % MnO2, High Grade 46 - 48% Mn, Medium grade 42 - 44 % Mn, Low Grade 38 - 40 % Mn, Steel Mill Grade 28 - 35 % Mn, Fines + 30 % Mn |
 |
Quartz [ Code : VM - 003 ]
Chemical composition : Loss on Ignition 0.1%, SiO2 99.4%, Fe203 0.2% , Mixed Oxide as R2O3 0.4%, Al2O3 0.2%, CaO Traces, MgO Traces |
 |
Bauxite [ Code : VM - 004 ]
Chemical composition : Bauxite, Aluminium Ore(Al2O3) 55 - 60 %, Iron Ore (Fe) 2 - 9 %, Silica Ore (SiO2) 2- 5 %, Loss on Drying @ 105 °C 0.78, Loss on Ignition @ 950°C 28.29 |
 |
Calcite [ Code : VM - 005 ]
Chemical composition : Calcite Powder/Calcite Mineral of purity ranging from 88% to 99% CaCO3, to cater to the demand and specifications of our valued customers. We can provide Calcite powder up to 12 microns. |
 |
Bentonite Powder [ Code : VM - 006 ]
Chemical composition : Yield Point 16 M3/t Min, Bentonite Water Loss 15%ml Max, Moisture 15% Max, Wet Screen 200 mesh 2.5% Max, Dry Screen 100 mesh 98% Min |
 |
Dolomite-Powder [ Code : VM - 007 ]
Chemical composition : MgO: 20-21.5%, SiO2:0.8-1.75%, CaO:30-31%, Fe2O3:0.07%, Al2O3:0.03% , The hardness is 3.5-4. The specific gravity is 2.8-2.9. The density is 2.86g/cm 3 ~ 3.20g/cm 3. The refractive index is 1.505 ~ 1.743, The dolomite powder is from 100-400mesh. |
 |
China Clay [ Code : VM - 008 ]
Chemical composition : SiO2:49% max. Al2O3:36% Fe2O3:0.35% max. Natural whiteness:78 min. Fired whiteness:89 loss of ignition:12 2um:63% moisture:25% max. |
 |
Silica Sand [ Code : VM - 009 ]
Chemical composition : SiO2 99.00 % , Fe2O3 0.03 %, Al2o3 0.16 %, CaO 0.05 %, MgO 0.03 %, LOI 0.12 %, Na2O 0.05 %, K2O 0.02 % |
 |
Feldspar [ Code : VM - 010 ]
Chemical composition : Silica as SiO2 67.00% +/- 1%, Alumina as Al2O3 18.25% +/- 0.5%, Ferric Oxide as Fe2O3 0.06% +/- 0.02%, Calcium Oxide CaO 1.34% +/- 0.5%, Magnesium Oxide as MgO 0.6% +/- 0.05%, Sodium Oxide as Na2O 2.50% +-/ 0.50%, Potassium Oxide as K2O 10.00% +/- 1%, Loss on Ignition as LOI 0.40% +/- 0.5% |
 |
Gypsum [ Code : VM - 011 ]
Chemical composition : CaO : 39.1%, SO3 : 53.2%, Fe2O3 : 0.05%, Na2O : 0.56%, K2O : 0.1%, Sp. Gravity : 2.96%, Oil absorption : 20 |
|
|
|